Trilac® ABS-GF3000-BK 30% Fiberglass Black ABS Resin
Subcategory: ABS Polymer; Filled/Reinforced Thermoplastic; Polymer; Thermoplastic
| Physical Properties | Metric | English | Comments |
|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.001 cm/cm | 0.001 in/in | ASTM D955 |
Mechanical Properties |
|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 70.3 MPa | 10200 psi | ASTM D638 |
| Flexural Modulus | 6.21 GPa | 901 ksi | ASTM D790 |
| Flexural Yield Strength | 106.9 MPa | 15500 psi | ASTM D790 |
| Izod Impact, Notched | 0.43 J/cm | 0.806 ft-lb/in | at 1/8 in (3.2 mm); ASTM D256 |
Thermal Properties |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96 °C | 205 °F | ASTM D648 |
Some of the values displayed above may have been converted from their original units and/or rounded in
order to display the information in a consistant format. Users requiring more precise data for scientific or
engineering calculations can click on the property value to see the original value as well as raw conversions
to equivalent units. We advise that you only use the original value or one of its raw conversions in your
calculations to minimize rounding error. We also ask that you refer to our disclaimer and terms of use
regarding this information. Click here to
view all the property values for this datasheet as they were originally entered.
These test results are believed to be based on reliable procedures. Due to variable conditions or methods of processing,
NO GUARANTEES OR WARRANTIES ARE EXPECTED OR IMPLIED, INCLUDING THE IMPLIED WARRANTY OF MERCHANTABILITY AND FITNESS FOR PARTICULAR PURPOSE.
The above information is not to be construed as a license or a recommendation to infringe on any patents. Typical properties are for natural,
unpigmented resins unless otherwise stated.
Actual processing conditions will depend on machine size, mold design, material residence time, and shot size. The settings
shown should serve as a guide to achieve the necessary stock temperatures for stable processing and good product quality. Stock melt
temperatures taken with a hand pyrometer is the best guide for selection of optimum operating conditions.
|
|